鋼號

C

Si

Mn

P≤

S≤

Cr

Mo

Ni

其它

SUS201

≤0.15

≤1.00

5.5-7.5

0.06

0.03

16-18

-

3.5-5.5

N≤0.25

202

≤0.15

≤1.00

7.5-10.0

0.06

0.03

17-19

-

4.0-6.0

N≤0.25

301

≤0.15

≤1.00

≤2.00

0.045

0.03

16-18

-

6.0-8.0

-

302

≤0.15

≤1.00

≤2.00

0.045

0.03

17-19

-

8-10.0

-

303

≤0.15

≤1.00

≤2.00

0.2

≥0.015

17-19

≤0.6

8.0-10.0

-

304

≤0.08

≤1.00

≤2.00

0.045

0.03

18-20

-

8-1.0.5

-

304L

≤0.03

≤1.00

≤2.00

0.045

0.03

18-20

-

9-13

-

305

≤0.12

≤1.00

≤2.00

0.045

0.03

17-19

-

10.5-13

-

309S

≤0.08

≤1.00

≤2.00

0.045

0.03

22-24

-

12-15

-

310S

≤0.08

≤1.5

≤2.00

0.045

0.03

24-26

-

19-22

-

316

≤0.08

≤1.00

≤2.00

0.045

0.03

16-18

2-3

10-14

-

316L

≤0.03

≤1.00

≤2.00

0.045

0.03

16-18

2-3

12-15

-

317

≤0.08

≤1.00

≤2.00

0.045

0.03

18-20

3-4

11-15

-

317L

≤0.03

≤1.00

≤2.00

0.045

0.03

18-20

3-4

11-15

-

321

≤0.08

≤1.00

≤2.00

0.045

0.03

17-19

-

9-13

Ti≥5×C

405

≤0.08

≤1.00

≤1.00

0.04

0.03

11.5-14.5

-

≤0.6

AL0.1-0.3

420F

0.26-0.4

≤1.00

≤1.25

0.06

≥0.15

12-14

≤0.6

≤0.6

-

430

≤0.12

≤0.75

≤1.00

0.04

0.03

16-18

-

≤0.6

-

 1Cr18Ni9Ti

有良好的耐(nai)熱(re)(re)性(xing)及(ji)抗腐蝕性(xing)。作加熱(re)(re)爐管、燃(ran)燒室簡體，遭(zao)火爐罩

 0Cr17Ni12Mo2

高(gao)溫具有優良的蠕變強度，作熱交換(huan)用部件，高(gao)溫耐(nai)蝕(shi)類螺(luo)拴

 0Cr25Ni20

比0Cr23Nil3抗氧化(hua)性好(hao)，可承受1235℃加熱(re)。爐用材(cai)料(liao)，汽車(che)凈化(hua)裝(zhuang)置(zhi)用材(cai)料(liao)

 2Cr23Ni13

承受980℃以下反復(fu)加(jia)熱(re)的抗氧化鋼(gang)。加(jia)熱(re)爐部件，重(zhong)油燃燒器

 0Cr19Ni9

通用耐氧化鋼，可承受870℃以下反復加熱

 0Cr18Ni11Ti

作在(zai)400～900℃腐蝕(shi)條件下使用的(de)部件，高溫用焊接結構(gou)部件

 0Cr18Ni11Nb

作在400～900℃腐蝕(shi)條件下(xia)使用(yong)的部件，高(gao)溫(wen)用(yong)焊接結(jie)構部件

 5Cr21Mn9Ni4N

以經受高(gao)溫強度為主的(de)汽(qi)油(you)及柴油(you)機用排氣(qi)閥

 Y5Cr21Mn9Ni4N

以經受高(gao)溫強度為主的汽油(you)及柴油(you)機用排氣閥

 2Cr22Ni11N

以(yi)抗氧(yang)化(hua)為主的汽油及柴油機用排(pai)氣(qi)閩